The composite was obtained by diffusion welding (DW) of a package with U-shaped elements (Fig. 1) from foils of alloy Nb–0.1 wt.% C 50 μm thick and Al 10 μm thick. Sapphire fibers with a diameter of ~0.25 mm, grown by the Stepanov method, were placed inside the Al elements. The DW of the packages was carried out according to the following regime: 600°C, 3 h at a pressure of 5.6 MPa + 1400°C, 30 min / 10.5 MPa