Flux Growth, Thermal Properties, and Luminescence Spectra of (Er,Yb,Lu)Al3(BO3)4 Solid Solutionsстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 4 сентября 2018 г.
Аннотация:We have studied phase relations in the pseudoquaternary system LuAl3(BO3)4–(K2Mo3O10–
Al2O3–B2O3) in the temperature range 1130 to 900°C. The phase relations were represented in graphical form, as a projection of the formation of solid phases in this range onto the composition triangle at 900°C.Optimal results in terms of high-temperature solution growth have been obtained at 25 wt.% LuAl3(BO3)4 in the growth charge. Undoped and erbium–ytterbium codoped LuAl3(BO3)4 (LuAB) single crystals have been grown from high-temperature solutions on “pointlike” seeds. The (Er,Yb):LuAB crystals are similar in thermal properties and luminescence spectra to (Er,Yb):YAl3(BO3)4 and (Er,Yb):GdAl3(BO3)4 crystals and can be used in diode-pumped lasers operating in the nominally eye-safe spectral region 1.5–1.6 μm.