Structural, magnetic, and superconducting properties of pulsed-laser-deposition-grown La 1.85 Sr 0.15 CuO 4 / La 2 / 3 Ca 1 / 3 MnO 3 superlattices on (001)-oriented LaSrAlO 4 substratesстатья
Статья опубликована в высокорейтинговом журнале
Статья опубликована в журнале из списка Web of Science и/или Scopus- Авторы: Das S., Sen K., Marozau I., Uribe-Laverde M.A., Biskup N., Varela M., Khaydukov Y., Soltwedel O., Keller T., Döbeli M.
- Журнал: Physical Review B
- Том: 89
- Номер: 9
- Год издания: 2014
- Издательство: American Physical Society
- Местоположение издательства: United States
- DOI: 10.1103/physrevb.89.094511
- Аннотация: Epitaxial La1.85Sr0.15CuO4/La2/3Ca1/3MnO3 (LSCO/LCMO) superlattices on (001)-oriented LaSrAlO4 substrates have been grown with pulsed laser deposition technique. Their structural, magnetic, and superconducting properties have been determined with in situ reflection high-energy electron diffraction, x-ray diffraction, specular neutron reflectometry, scanning transmission electron microscopy, electric transport, and magnetization measurements. We find that despite the large mismatch between the in-plane lattice parameters of LSCO (a = 0.3779 nm) and LCMO (a = 0.387 nm) these superlattices can be grown epitaxially and with a high crystalline quality. While the first LSCO layer remains clamped to the LaSrAlO4 substrate, a sizable strain relaxation occurs already in the first LCMO layer. The following LSCO and LCMO layers adopt a nearly balanced state in which the tensile and compressive strain effects yield alternating in-plane lattice parameters with an almost constant average value. No major defects are observed in the LSCO layers, while a significant number of vertical antiphase boundaries are found in the LCMOlayers. The LSCO layers remain superconducting with a relatively high superconducting onset temperature of T onset c ≈ 36 K. The macroscopic superconducting response is also evident in the magnetization data due to a weak diamagnetic signal below 10 K for H ab and a sizable paramagnetic shift for H c that can be explained in terms of a vortex-pinning-induced flux compression. The LCMO layers maintain a strongly ferromagnetic state with a Curie temperature of T Curie ≈ 190 K and a large low-temperature saturation moment of about 3.5(1) μB per Mn ion. These results suggest that the LSCO/LCMO superlattices can be used to study the interaction between the antagonistic ferromagnetic and superconducting orders and, in combination with previous studies on YBa2Cu3O7−x/La2/3Ca1/3MnO3 superlattices, may allow one to identify the relevant mechanisms.