Amorphization of Vanadium Oxides during the Reversible Insertion of Lithiumстатья
Информация о цитировании статьи получена из
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 7 июля 2021 г.
Аннотация:The results of studying the structure and phase composition of thin-film positive electrodes of alithium-ion battery based on vanadium oxides are presented. It is shown that initially polycrystalline filmscontain higher V2O5 and V3O7 oxides, the proportion of which increases with the time of oxygen annealing.As a result of charge–discharge cycling, the higher vanadium oxides are amorphized, while the content of theVO2 and V2O3 phases decreases slightly, and the proportion of VO oxide remains unchanged. These data arein good agreement with the change in the capacity of the films during their cycling, which suggests that themain reason for the decrease in the capacity of the films is the amorphization of the higher vanadium oxideswith the highest specific capacity.