Tuning the morphology and magnetic properties of single-domain SrFe8Al4O19 particles prepared by citrate auto-combustion routeстатья
Информация о цитировании статьи получена из
Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 12 января 2022 г.
Аннотация:Single-domain particles of SrFe8Al4O19 were prepared by thermal treatment at 1473 K of porous products of citrate-nitrate auto-combustion, and the influence of synthesis time on the particle morphology and magnetic properties was studied. The procedure allows to obtain SrFe8Al4O19 particles with mean diameters 100 - 460 nm, and their coercivity ranges from 14.5 to 18.4 kOe, while ferromagnetic resonance frequencies vary from 149 to 164 GHz.DOI: 10.1016/j.mencom.2021.03.025