Rheological evidence of gel formation in dilute poly(acrylonitrile) solutionsстатья
Статья опубликована в высокорейтинговом журнале
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:Rheological studies of low concentration (down to 0.1%) poly-(acrylonitrile) (PAN)−dimethyl sulfoxide (DMSO) solutions revealed the existence of a rather unusual effect of the gel-like structure formation, while this phenomenon is absent at higher concentrations (17−24 wt %) of PAN in DMSO. The evidence of the gel-like structure consists in the pronounced yielding, which can be detected in the 0.1−5% concentration range and plateau on the frequency dependence of the storage modulus. In addition, rather large particles were found by the dynamic light scattering method. The gel-like structure of dilute PAN solutions is similar to supramolecular gels, while the gelation of water containing systems brings to mind a phase transition. The observed maximal Newtonian viscosity at the low shear stresses for dilute solutions should be treated as an artifact related to the method of measuring, and at long-term loading the plateau is converted to the yield stress. Dilute PAN/DMSO gels are thixotropic. A possibility of bifurcation (due to coexistence of different states) leads
to self-oscillations of the stress response in a wide shear rate region. The dynamic viscosity coincides with the shear apparent viscosity for high concentrations but does not in the low concentration range. Such a kind of rheological behavior is not observed
if dimethylformamide or aqueous solution of sodium thiocyanate was used instead of DMSO as a PAN solvent. Possible chemical structures responsible for the gel structure formation are discussed.