Bioceramics Based on β-Calcium Pyrophosphateстатья
Статья опубликована в высокорейтинговом журнале
Информация о цитировании статьи получена из
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 мая 2022 г.
- Авторы: Safronova Tatiana, Kiselev Andrey, Selezneva Irina, Shatalova Tatiana, Lukina Yulia, Filippov Yaroslav, Toshev Otabek, Tikhonova Snezhana, Antonova Olga, Knotko Alexander
- Журнал: Materials
- Том: 15
- Номер: 9
- Год издания: 2022
- Издательство: MDPI
- Местоположение издательства: Basel, Switzerland
- Первая страница: 1
- Последняя страница: 24
- Номер статьи: 3105
- DOI: 10.3390/ma15093105
- Аннотация: Ceramic samples based on β-calcium pyrophosphate β-Ca2P2O7 were prepared from powders of γ-calcium pyrophosphate γ-Ca2P2O7 with preset molar ratios Ca/P = 1, 0.975 and 0.95 using firing at 900, 1000, and 1100 °C. Calcium lactate pentahydrate Ca(C3H5O3)2⋅5H2O and monocalcium phosphate monohydrate Ca(H2PO4)2⋅H2O were treated in an aqua medium in mechanical activation conditions to prepare powder mixtures with preset molar ratios Ca/P containing calcium hydrophosphates with Ca/P = 1 (precursors of calcium pyrophosphate Ca2P2O7). These powder mixtures containing calcium hydrophosphates with Ca/P = 1 and non-reacted starting salts were heat-treated at 600 °C after drying and disaggregation in acetone. Phase composition of all powder mixtures after heat treatment at 600 °C was presented by γ-calcium pyrophosphate γ-Ca2P2O7 according to the XRD data. The addition of more excess of monocalcium phosphate monohydrate Ca(H2PO4)2·H2O (with appropriate molar ratio of Ca/P = 1) to the mixture of starting components resulted in lower dimensions of γ-calcium pyrophosphate (γ-Ca2P2O7) individual particles. The grain size of ceramics increased both with the growth in firing temperature and with decreasing molar ratio Ca/P of powder mixtures. Calcium polyphosphate (t melt = 984 °C), formed from monocalcium phosphate monohydrate Ca(H2PO4)2⋅H2O, acted similar to a liquid phase sintering additive. It was confirmed by tests in vitro that prepared ceramic materials with preset molar ratios Ca/P = 1, 0.975, and 0.95 and phase composition presented by β-calcium pyrophosphate β-Ca2P2O7 were biocompatible and could maintain bone cells proliferation. Keywords: calcium lactate pentahydrate; monocalcium phosphate monohydrate; mechanical activation; powder; brushite; monetite; calcium pyrophosphate; ceramics; biocompatibility
- Добавил в систему: Сафронова Татьяна Викторовна
Прикрепленные файлы
| № | Имя | Описание | Имя файла | Размер | Добавлен |
|---|---|---|---|---|---|
| 1. | materials-15-03105-v3.pdf | materials-15-03105-v3.pdf | 7,7 МБ | 14 декабря 2022 [safronova] | |
| 2. | Graf.jpg | Graf.jpg | 385,7 КБ | 25 апреля 2022 [safronova] | |
| 3. | Publication_Certificate_MDPI_materials-15-03105.pdf | Publication_Certificate_MDPI_materials-15-03105.pdf | 221,8 КБ | 25 апреля 2022 [safronova] | |
| 4. | Article_Banner_MDPI_materials-15-03105.pdf | Article_Banner_MDPI_materials-15-03105.pdf | 34,9 КБ | 25 апреля 2022 [safronova] | |
| 5. | materials-1626578-Updated_2.0_10_05_2022.pdf | materials-1626578-Updated_2.0_10_05_2022.pdf | 7,7 МБ | 10 мая 2022 [safronova] |