Magnetic properties and magnetoresistance of hybrid multilayer nanostructures {[(Co40Fe40B20)34(SiO2)66]/[ZnO]}nстатья
Дата последнего поиска статьи во внешних источниках: 10 июля 2024 г.
- Авторы: Kalinin Y.E., Sitnikov A.V., Makagonov V.A., Foshin V.A., Volochaev M.N., Pripechenkov I.M., Perova N.N., Ganshina E.A., Rylkov V.V., Granovsky A.B.
- Журнал: Journal of Magnetism and Magnetic Materials
- Номер: 604
- Год издания: 2024
- Издательство: Elsevier BV
- Местоположение издательства: Netherlands
- Номер статьи: 172287
- DOI: 10.1016/j.jmmm.2024.172287
- Аннотация: The structural, electrical, magnetic, magneto-optical properties and magnetoresistance of {[(Co40Fe40B20)34( SiO2)66]/[ZnO]}n multilayer structures, where n = 50 is the number of bilayers (Co40Fe40B20)34(SiO2)66 nano composite and ZnO have been studied. The thicknesses of (Co40Fe40B20)34(SiO2)66 nanocomposite layers as well as ZnO spacers were varied in a wide range. The samples were synthesized by ion-beam sputtering onto glass ceramic substrates. The (Co40Fe40B20)34(SiO2)66 composite have an amorphous structure and the semiconductor ZnO interlayers have a hexagonal crystalline structure with the p63mc symmetry group. The nanocomposite layers containing a ferromagnetic component far from the percolation threshold are in a superparamagnetic state. The presented in the paper data of magnetization, magneto-optical transverse Kerr effect and magneto resistance indicates that long-range ferromagnetic order does not form down to 77 K both for references ZnO films and studied multilayers with thin and thick ZnO interlayers. An increase in the magneto-optical signal in multilayers compared to references (Co40Fe40B20)34(SiO2)66 composite films has been detected at 1.2 eV. The magnetoresistance of {[(Co40Fe40B20)34(SiO2)66]/[ZnO]}n multilayers with thick (>32 nm) ZnO interlayers is lower than in reference (Co40Fe40B20)34(SiO2)66 nanocomposite, while at thin ZnO interlayers magnetoresistance is significantly higher and reaches 12 % at temperatures of 77 К. Possible mechanisms of ferromagnetic and antiferromagnetic ordering, enhancement of the magneto-optical response and magnetoresistance in {[(Co40Fe40B20)34(SiO2)66]/[ZnO]}n multilayer nanostructures are discussed.