Slip-Jump Model for Carbon Combustion Synthesis of Complex Oxide Nanoparticlesстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 17 января 2018 г.
Аннотация:Carbon Combustion Synthesis of Oxides (CCSO) is a promising method to produce submicron- and nano-sized complex oxides. The CCSO was successfully utilized for producing several complex oxides, a complete theoretical model including the sample porosity, flow parameters and reaction energetics is needed to predict the combustion parameters for CCSO. In this work, we studied the ignition temperature and combustion wave axial temperature distribution, activation energy, combustion heat and thermal losses for a typical CCSO synthesis for cylindrical samples of Ni-Zn ferrites with high (>85%) porosity. We developed a two level combustion model of chemically active nano-dispersed mixture, using the experimentally measured ignition temperature and combustion parameter values utilizing the slip-jump method for high Knudsen numbers. The theoretical predictions of highly porous samples when the flow resistivity is small and the gas can easily flow through the cylindrical sample are in good agreement with the experimental data. The calculation of combustion characteristics for the lower porosity values demonstrated that the surface combustion was dominated due to high gas flow resistivity of the sample. Finger combustion features were observed at this combustion mode.